Conductive nanoparticles

ABSTRACT

Isolated conductive nanoparticles on a dielectric layer and methods of fabricating such isolated conductive nanoparticles provide charge storage units in electronic structures for use in a wide range of electronic devices and systems. The isolated conductive nanoparticles may be used as a floating gate in a flash memory. In an embodiment, conductive nanoparticles are deposited on a dielectric layer by a plasma-assisted deposition process such that each conductive nanoparticle is isolated from the other conductive nanoparticles to configure the conductive nanoparticles as charge storage elements.

TECHNICAL FIELD

This application relates generally to semiconductor devices and device fabrication.

BACKGROUND

Generation of higher capacity electronic devices and systems rely on scaling down device dimensions to realize higher density memory devices. However, associated with increased device density due to closer spacing is word line coupling within the higher density memories. Techniques are needed to reduce word line coupling, reduce programming voltages, and enable continued scaling of devices within a memory.

SUMMARY

The abovementioned problems are addressed by embodiments of the present invention and will be understood by reading and studying the following specification. An embodiment for a method of forming an electronic device includes forming a dielectric layer in an integrated circuit and forming conductive nanoparticles on the dielectric layer to generate a charge storage layer, in which each conductive nanoparticle is isolated from the other conductive nanoparticles. In an embodiment, conductive nanoparticles may be formed by a plasma-assisted deposition process. Embodiments of structures and methods for forming such structures provide for transistors, memory devices, and electronic systems having isolated conductive nanoparticles on a dielectric layer to store charge. These and other aspects, embodiments, advantages, and features will become apparent from the following description and the referenced drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 depicts features of an embodiment of a method to form conductive nanoparticles on a dielectric layer to generate a charge storage layer.

FIGS. 2A, 2B illustrate SEM images of an embodiment of platinum nanoparticles at 650° C. and 750° C.

FIGS. 3A, 3B illustrate SEM images of an embodiment of platinum nanoparticles at 850° C. and 950° C.

FIG. 4A depicts an embodiment of a configuration of a floating gate transistor having isolated conductive nanoparticles as its floating gate.

FIG. 4B depicts an embodiment of a three-dimensional structure of isolated conductive nanoparticles.

FIG. 5 is a simplified block diagram for an embodiment of an electronic system having a controller coupled to an electronic device, where the controller and/or the electronic device have a charge storage unit configured as isolated conductive nanoparticles on a dielectric layer.

FIG. 6 illustrates a block diagram for an embodiment of an electronic system having a charge storage unit configured as isolated conductive nanoparticles on a dielectric layer.

DETAILED DESCRIPTION

The following detailed description refers to the accompanying drawings that show, by way of illustration, specific aspects and embodiments in which the present invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the present invention. Other embodiments may be utilized and structural, logical, and electrical changes may be made without departing from the scope of the present invention. The various embodiments are not necessarily mutually exclusive, as some embodiments can be combined with one or more other embodiments to form new embodiments.

The terms “wafer” and “substrate” used in the following description include any structure having an exposed surface with which to form an integrated circuit (IC) structure. The term “substrate” is understood to include semiconductor wafers. The term “substrate” is also used to refer to semiconductor structures during processing, and may include other layers that have been fabricated thereupon. Both wafer and substrate include doped and undoped semiconductors, epitaxial semiconductor layers supported by a base semiconductor or insulator, as well as other semiconductor structures well known to one skilled in the art. The term “conductor” is understood to generally include n-type and p-type semiconductors and the term “insulator” or “dielectric” is defined to include any material that is less electrically conductive than the materials referred to as conductors.

Herein, a nanoparticle includes a material structure whose effective diameter is measured in the nanometer range. A nanoparticle may have an effective diameter as large as 20 nanometers. Depending on the unit cell for a material, a nanoparticle of the material may include the material configured as a nanocrystal. A conductive nanoparticle is a material structured as a nanoparticle, where the material when structured in bulk form is conductive. These conductive nanoparticles are able to trap charges.

In an embodiment, a charge storage unit of an electronic device includes conductive nanoparticles on a dielectric layer, in which each conductive nanoparticle is isolated from the other conductive nanoparticles. The conductive nanoparticles may be deposited by plasma-assisted deposition techniques, which may include, but are not limited to, plasma-enhanced chemical vapor deposition (PECVD), plasma-enhanced atomic layer deposition (PEALD), and physical vapor deposition (PVD). The application of a plasma may be used to roughen the deposited particles to form the nanoparticles. Further, the application of the plasma may provide for a higher density of conductive nanoparticles and improved adhesion for subsequent processing.

A charge storage unit may include a capping dielectric on the conductive nanoparticles with the conductive nanoparticles as charge storage elements. With the base dielectric layer sufficiently thin, charges may tunnel through the base dielectric layer and be trapped in the nanoparticles. The capping dielectric provides isolation from conductive elements such that the trapped charge may be stored, until an appropriate stimulus is provided to release the charge. In an embodiment, conductive nanoparticles may be used as a floating gate to replace the use of a polysilicon floating gate that is currently being used in flash memory. The isolated conductive nanoparticles may serve as a charge trapping layer to reduce programming voltage and to reduce word line coupling, as well as to enable continued scaling beyond that associated with the conventional floating gate structure.

FIG. 1 shows features of an embodiment of a method to form conductive nanoparticles on a dielectric layer to generate a charge storage unit. At 110, a dielectric layer is formed in an integrated circuit on a substrate. In an embodiment, the dielectric layer may be a silicon oxide layer. Alternatively, the dielectric layer may be a layer of a high-κ dielectric materials. High-κ materials include materials having a dielectric constant greater than silicon dioxide, for example, dielectric materials having a dielectric constant greater than about twice the dielectric constant of silicon dioxide. A set of high-κ dielectric may include, but is not limited to, HfO_(x), ZrO_(x), TiO_(x), TaO_(x), LaAlO_(x), the lanthanide oxides, other metal oxides, and corresponding metal silicates. The dielectric layer may be a layer of an insulative nitride and/or insulative oxynitride. The dielectric layer may be structured as a dielectric stack having a number of layers of different dielectric material. The dielectric stack may be nanolaminate. The term “nanolaminate” means a composite film of ultra thin layers of two or more materials in a layered stack. Typically, each layer in a nanolaminate has a thickness of an order of magnitude in the nanometer range. Further, each individual material layer of the nanolaminate may have a thickness as low as a monolayer of the material or as high as 20 nanometers. In an embodiment, the dielectric layer formed may be structured as a tunneling dielectric allowing the movement of charge through the dielectric under appropriate stimulation. In an embodiment, a tunneling dielectric may have a thickness of 30 Å or less.

At 120, conductive nanoparticles are deposited on the dielectric layer by a plasma assisted deposition process such that each conductive nanoparticle is isolated from the other conductive nanoparticles. The conductive nanoparticles are configured as isolated material islands forming a charge storage layer. This charge storage layer may be covered by a top dielectric layer isolating the conductive nanoparticles, not only from each other, but from direct contact with a conductive medium. In an embodiment, the top dielectric layer may be of the same construction as the dielectric layer on which the conductive nanoparticles are deposited so as to effectively form one dielectric layer with conductive nanoparticles dispersed in the one dielectric layer. In an embodiment, the conductive nanoparticles are configured substantially in a plane on the dielectric layer. Alternatively, the conductive nanoparticles may be configured dispersed throughout a dielectric layer having at least a minimal distance from the bottom of the dielectric layer that is formed on a substrate.

In an embodiment, the size of the nanoparticles is increased by annealing to form isolated agglomerations of particles defining isolated enlarged islands of conductive material. In an embodiment, the size of the nanoparticles may be increased by a factor of about five. Enlargement by annealing is not limited to a factor of five, but may use other factors depending on the application. In an embodiment, a nanoparticle may have an effective or average diameter of about 2 nm that may be enlarged to about 10 nm by annealing. Nanoparticles are not limited to these dimensions, but may have other dimensions in various embodiments. The isolated structures, either as conductive nanoparticles or enlarged islands of conductive material, provide a means to reduce an effect associated with a defect that allows charge to leak through the dielectric on which the nanoparticles are formed. In a structure having isolated conductive nanoparticles, leakage may be localized to a few of these nanoparticles, reducing the amount of charge that may leak due to a defect, which may amount to only a few electrons. In an embodiment, conductive nanoparticles may be deposited by PECVD. In an embodiment, conductive nanoparticles may be deposited by PEALD. In an embodiment, conductive nanoparticles may be deposited by ALD followed by exposure to a plasma. In an embodiment, material may be deposited by ALD followed by exposing the material to a plasma to form nanoparticles. The material deposited by ALD may be in the form of nanoparticles, where the subsequent exposure to a plasma enhances the density of the nanoparticles. Herein, a process that includes atomic layer deposition followed by exposure to a plasma is referred to as plasma agglomerated atomic layer deposition or plasma agglomerated ALD. Though the exposure to a plasma in plasma agglomerated ALD may be post deposition with respect to a number of ALD deposition cycles, plasma agglomerated ALD is herein defined as a plasma-assisted deposition process. The flow of precursors in these plasma-assisted methods is controlled to provide for the formation of isolated nanoparticles such that a uniform layer of the deposited material is not formed.

In an embodiment, ruthenium nanoparticles are deposited on a dielectric layer using plasma assisted chemical vapor deposition. A capping dielectric layer may be formed on the ruthenium nanoparticles to create a charge storing unit. During processing subsequent to nanoparticle deposition, such as the formation of the capping dielectric layer, some of the ruthenium nanoparticles may oxidize. However, the oxidation may form conductive ruthenium oxide nanoparticles, which are applicable as conductive nanoparticles. Thus, selecting conductive nanoparticles that remain conductive on oxidation eases the constraints on subsequent processing.

In an example embodiment, ruthenium nanoparticles may be formed at a temperature of about 200° C. The processing wafer may be soaked in argon at 10 Torr for 2 minutes, after which a 30 second 200 sccm flow for 300 W Ar plasma may be conducted to stabilize the plasma. Then, a (C₆H₈)Ru(CO)₃ reactants may be switched to the reactant chamber at the same time as the argon is turned off. The delivery lines to a showerhead, held at about 50° C., may be heated to about 62° C. A 500 sccm He carrier gas may be used. The reactants may be controlled to flow for about 2 seconds providing ruthenium nanoparticles with a density of approximately 4×10¹²/cm² (100-110 nanocrystals/50 nm×50 nm area). This is an example embodiment, other embodiments are not limited to these precursors and process parameters.

In an embodiment, ruthenium nanoparticles deposited on a dielectric layer may be capped with a dielectric layer. In various embodiments, the dielectric layer may be a plasma-enhanced tetraethylorthosilicate (PE-TEOS), a silicon oxide in the form of a high density plasma (HDP) oxide, a silicon oxide in the form of a high temperature oxide (HTO), a low temperature ALD oxide, a high temperature (such as 600° C.) ALD oxide, or a combination of an ALD oxide between the ruthenium nanoparticles and one of the other dielectric layers. A capping dielectric layer may be characteristic by the method used to form the capping dielectric layer. Charge storage structures including a capping dielectric layer on ruthenium nanoparticles deposited on a dielectric layer may have a range of program erase (P/E) windows.

In an embodiment, platinum nanoparticles may be deposited on a dielectric layer using plasma assisted chemical vapor deposition. In an example embodiment, platinum nanoparticles may be formed at a temperature of about 200° C. The processing wafer may be soaked in argon at 10 Torr for 2 minutes, after which a 30 second 200 sccm flow for 300 W Ar plasma may be conducted to stabilize the plasma. Then, (CH₃)₃(CH₃C₅H₄)Pt and O₂ reactants may be switched to the reactant chamber at the same time as the argon is turned off. The delivery lines to a showerhead, held at about 50° C., may be heated to about 60° C. A 100 sccm He carrier gas may be used. The reactants may be controlled by flow for about 8 seconds providing platinum nanoparticles with a density of approximately 4×10²/cm² (100-110 nanocrystals/50 nm×50 nm area). This is an example embodiment, other embodiments are not limited to these precursors and process parameters.

In an embodiment, platinum nanoparticles deposited on a dielectric layer may be capped with a dielectric layer. In various embodiments, the dielectric layer may be a PE-TEOS, a HDP oxide, a HTO oxide, a low temperature ALD oxide, a high temperature ALD oxide, or a combination of an ALD oxide between the platinum nanoparticles and one of the other dielectric layers. Structures including a capping dielectric layer on platinum nanoparticles deposited on a dielectric layer may have a range of P/E windows. In an embodiment, platinum nanoparticles on a dielectric layer with a top ALD oxide may provide a program/erase window of about 3.2 volts using 15V, 1 sec pulses with no degradation during subsequent cycles.

In an embodiment, platinum nanoparticles may be deposited on a dielectric layer using physical vapor deposition. The physical vapor deposition may be performed in short doses to provide the nanoparticles. A platinum sputter target may be exposed to an argon plasma for about 1-2 seconds to provide nanoparticles on a dielectric layer, where the nanoparticles are separated from each other. Other dosing periods may be used to provide spaced-apart platinum nanoparticles. PVD processing of platinum nanoparticles may be formed in a vacuum or at appropriately low pressures. In an embodiment, platinum nanoparticles may be processed by PVD at a pressure ranging from about 10⁻⁷ Torr to about 10⁻⁸ Torr. Other conductive elements and conductive combinations of elements may be used in a PVD process to provide spaced-apart conductive nanoparticles.

In an embodiment, platinum nanoparticles may be deposited on a dielectric layer using atomic layer deposition. Controlling nucleation sites for the platinum nanoparticles may provide spaced-apart platinum nanoparticles. The formation of the nanoparticles by ALD may be followed by other processes, such as plasma exposure, annealing, or combinations of post deposition processes, to enhance the density of the platinum nanoparticles.

In an embodiment, cobalt nanoparticles may be deposited on a dielectric layer using plasma agglomerated atomic layer deposition. ALD processing provides nucleation mechanism for generating the nanoparticles as isolated islands. A number of ALD cycles may be performed followed by exposure to a plasma for a given amount of time. An ALD cycle for depositing cobalt may consist of independently pulsing a cobalt-containing precursor, a purge gas, a reactant precursor, and another purge gas. Pulsing purge gases is performed to remove precursors and by-products from the reaction chamber after the precursors have been pulsed into the chamber for a specific time. For additional aid in removal of material, the purge pulse may be followed by evacuating the reaction chamber for a short period to pump out by-products and excess precursors. In an example embodiment, cobalt nanoparticles may be formed at a substrate temperature of about 325° C. in an ALD reactant chamber with the showerhead held at about 50° C. The ALD cycle may include a 4 sec pulse of CpCo(CO)₂, where the cyclopentadienyl (Cp) ligand is a monoanionic ligand with the formula C₅H₅. The CpCo(CO)₂ pulse may be followed by a 5 sec Ar purge followed by a 60 sec evacuation pump. After the purge/pump for the cobalt-containing precursor, a 2 sec NH₃ reactant precursor may be pulsed followed a 5 sec argon purge and a 10 sec evacuation pump to complete a cycle. In an embodiment, after conducting 10 cycles the deposited material may be exposed to a 10 second 300 watt 300 sccm Ar plasma to form cobalt nanoparticles. This is an example embodiment, other embodiments are not limited to these precursors and process parameters.

To form a charge storage unit, a capping dielectric may be formed on the cobalt nanoparticles. During the capping process or in subsequent processing, some cobalt nanoparticles may oxidize eliminating such structures as conductive nanoparticles. Processing at low temperatures may aid in reducing the amount of cobalt nanoparticles that oxidize. Further, choice of dielectrics used in the charge storage unit may aid in reducing the amount that the cobalt nanoparticles oxidize. Using dielectrics that do not contain oxygen, such as silicon nitride, may reduce any tendency for cobalt nanoparticles to oxidize. Alternatively, silicon oxide may be used for a tunneling oxide and a capping oxide with a barrier, or liner, layer between the cobalt nanoparticles and these oxides. Metal oxides may be used in which the metal oxygen bonding is structurally preferred such that cobalt nanoparticles do not oxidize as the metal oxide is formed on the cobalt nanoparticles.

In an embodiment, the size of conductive nanoparticles may be increased by annealing. In an embodiment, platinum nanoparticles remain stable in an N₂O atmosphere up to 650° C., but may begin to form an agglomeration at 750° C. FIGS. 2A, 2B illustrate SEM images of platinum nanoparticles at 650° C. and 750° C. In a NH₃ atmosphere, platinum nanoparticles may be stable up to 850° C., but may begin incremental agglomeration at 25° C. intervals above 850° C., with large crystals and spacing occurring at 950° C. FIGS. 3A, 3B illustrate SEM images of platinum nanoparticles at 850° C. and 950° C. By selectively controlling annealing, different formats for isolated conductive material may be formed allowing the selection of dense conductive nanoparticles or enlarged islands of conductive material with larger spacing, depending on the application. The spacing between isolated conductive regions may be correlated to the effective diameter of these isolated conductive regions.

FIG. 4A shows an embodiment of a configuration of a floating gate transistor 400 having isolated conductive nanoparticles 405 as its floating gate. Transistor 400 includes a silicon based substrate 410 with a source 420 and a drain 430 separated by a body region 432. However, transistor 400 is not limited to silicon based substrates, but may be used with a variety of semiconductor and insulating substrates. Body region 432 between source 420 and drain 430 defines a channel region having a channel length 434. Located above body region 432 is a stack 455 including a gate dielectric 440, conductive nanoparticles 405 as a floating gate, a floating gate dielectric 442, and a control gate 450. An interfacial layer 433 may form between body region 432 and gate dielectric 440. In an embodiment, interfacial layer 433 may be limited to a relatively small thickness compared to gate dielectric 440, or to a thickness significantly less than gate dielectric 440 as to be effectively eliminated.

Conductive nanoparticles 405 may be structured as a layer of spaced-apart conductive particles. Alternatively, the conductive nanoparticles may be structured as a number of layers of spaced-apart conductive particles. In an embodiment, the number of layers, or thickness of the film of isolated conductive nanoparticles, is selected to provide charge trapping to the various levels of conductive nanoparticles by a tunneling mechanism. Such a thickness or distance from body region 432 is dependent on the application. Conductive nanoparticles 405 may include, but are not limited to, platinum nanoparticles, ruthenium nanoparticles, conductive ruthenium oxide nanoparticles, nanoparticles of other transition metals (W, Ni, etc.), noble metals (Rh, Ir, Pd, etc.), conductive metal oxides, conductive nitrides, and other conductive compounds.

Gate dielectric 440 may be configured as a tunneling dielectric. In an embodiment, gate dielectric 440 has a thickness, measured as the shortest distance from body region 432 to a conductive nanoparticle, of 30 Å or less. In an embodiment, floating dielectric 442 has a thickness, measured as the shortest distance from control gate 450 to a conductive nanoparticle, between about 100 Å and about 150 Å. Gate dielectric 440 and floating gate 442 made be composed of the same component materials or different component materials. The insulating materials selected for gate dielectric 440 and floating gate dielectric 442 may be selected to reduce or eliminate oxidation of the conductive nanoparticles during processing subsequent to their formation. The material for gate dielectric 440 and floating gate dielectric 442 may include, but is not limited to, silicon oxide, insulating nitrides, insulating oxynitrides, and high-κ dielectric materials. Gate dielectric 440 and floating gate dielectric 442 may each be structured as a single dielectric layer or as a dielectric stack.

Various embodiments for charge storage units using isolated conductive nanoparticles on a dielectric layer may provide for enhanced device performance by providing devices with reduced leakage current. In a floating gate transistor, a number of conductive nanoparticles replace a conventional floating gate that may be considered to be structured as a plate. Leakage for a conventional floating gate or for an embodiment of conductive nanoparticles may typically be determined by defects, which are not uniform in the structure. If the leakage is mainly by defects, then using isolated conductive nanoparticles, only a few of the nanoparticles are associated with the defects from which charge may leak. With a few associated leakage sites, such leakage may be ignored since it is associated with charge trapped in a few nanoparticles. However, with a conventional plate configuration, the entire plate is conductively coupled associating non-uniform defects with the entire plate such that charge may be conducted to the defects, increasing the amount of leakage charge. With a much lower leakage associated with the conductive nanoparticles as compared with the conventional floating gate, thinner gate dielectric 440 may be used with the conductive nanoparticles. Further, structures with thinner gate dielectric 440 also allow the use of lower voltages to program charge in floating transistor 400.

In an embodiment, conductive nanoparticles may be configured with a structure having three-dimensional features rather than a flat structure. A flat structure may be considered to be a planar structure whose three-dimensional aspect is provided by having a uniform or gradual-varying thickness. FIG. 4B shows an embodiment of a structure 460 having spaced-apart conductive nanoparticles 470 with three-dimensional features. Conductive nanoparticles 470 may be formed on a dielectric layer 480 having stud 490 protruding up from a surface 485 of dielectric layer 480. Conductive nanoparticles 470 may be disposed around vertical and horizontal sides of stud 490. Stud 490 is not limited to having perpendicular walls, but may be have various shapes protruding from surface 485 of dielectric layer 480. Various embodiments provide conductive nanoparticles as a charge storage unit configured in multiple planes or in a non-planar arrangement. Structure 460 may be used in the floating gate transistor 400 of FIG. 4A.

Additional improvements in leakage current characteristics may be attained by forming one or more of gate dielectric 440 and floating gate 442 in a nanolaminate structure. The transition from one layer of the nanolaminate to another layer of the nanolaminate provides further disruption to a tendency for an ordered structure in the nanolaminate stack, eliminating the occurrence of convenient paths from body region 432 to conductive nanoparticles 405.

Transistors and other devices having isolated conductive nanoparticles on a dielectric layer be implemented into memory devices and electronic systems including information handling devices. Embodiments of these information handling devices may include telecommunication systems, wireless systems, and computers.

FIG. 5 is a simplified block diagram for an embodiment of an electronic system 500 having a controller 505 coupled to an electronic device 525, where controller 505 and/or electronic device 525 have a charge storage unit configured as isolated conductive nanoparticles on a dielectric layer, in accordance with various embodiments. Electronic system 500 includes a bus 515, where bus 515 provides electrical conductivity between controller 505 and electronic device 525. Electronic system 500 may include, but is not limited to, information handling devices, wireless systems, telecommunication systems, fiber optic systems, electro-optic systems, and computers.

FIG. 6 illustrates a block diagram for an embodiment of an electronic system 600 having a charge storage unit configured as isolated conductive nanoparticles on a dielectric layer. System 600 may include a controller 605, a memory 625, an electronic apparatus 635, and a bus 615, where bus 615 provides electrical conductivity between controller 605 and electronic apparatus 635, and between controller 605 and memory 625. Bus 615 may include an address bus, a data bus, and a control bus, each independently configured. Alternatively, bus 615 may use common conductive lines for providing address, data, and/or control, the use of which is regulated by controller 605. In an embodiment, electronic apparatus 635 may be additional memory configured similar as memory 625. An embodiment may include an additional peripheral device or devices 645 coupled to bus 615. In an embodiment, controller 605 is a processor. In an embodiment, controller 605 is a processor having a memory. Any of controller 605, memory 625, bus 615, electronic apparatus 635, and peripheral device devices 645 may include an embodiment of a charge storage unit configured as isolated conductive nanoparticles on a dielectric layer. System 600 may include, but is not limited to, information handling devices, telecommunication systems, and computers.

Peripheral devices 645 may include displays, additional storage memory, or other control devices that may operate in conjunction with controller 605. Alternatively, peripheral devices 645 may include displays, additional storage memory, or other control devices that may operate in conjunction with controller 605 and/or memory 625.

Memory 625 may be realized as a memory device having a charge storage unit configured as isolated conductive nanoparticles on a dielectric layer, in accordance with various embodiments. It will be understood that embodiments are equally applicable to any size and type of memory circuit and are not intended to be limited to a particular type of memory device. In an embodiment, a flash memory may include an array of memory cells, each memory cell having a charge storage unit configured as isolated conductive nanoparticles on a dielectric layer. The conductive nanoparticles of a charge storage unit serve as a charge trapping layer instead of a structure having a polysilicon floating gate, as discussed with respect to embodiments associated with FIGS. 4A-4B. Each charge storage unit may be accessed using word lines, where the conductive nanoparticles provide for reduction of word line coupling. In addition, the conductive nanoparticles enable the use of reduced programming voltages and provide enhanced charge leakage characteristics. Such properties may provide for increased density of memory cells.

Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that any arrangement that is calculated to achieve the same purpose may be substituted for the specific embodiments shown. It is to be understood that the above description is intended to be illustrative, and not restrictive, and that the phraseology or terminology employed herein is for the purpose of description and not of limitation. Combinations of the above embodiments and other embodiments will be apparent to those of skill in the art upon studying the above description. 

1. A method of forming an electronic device, the method comprising: forming a dielectric layer in an integrated circuit on a substrate; and depositing conductive nanoparticles on the dielectric layer by a plasma-assisted deposition process such that each conductive nanoparticle is isolated from the other conductive nanoparticles to configure the conductive nanoparticles as charge storage elements.
 2. The method of claim 1, wherein depositing conductive nanoparticles includes depositing the conductive nanoparticles such that spacing between the conductive nanoparticles is at about an effective diameter of a conductive nanoparticle.
 3. The method of claim 1, wherein depositing conductive nanoparticles includes depositing metal nanoparticles.
 4. The method of claim 1, wherein depositing conductive nanoparticles includes depositing conductive metal oxide nanoparticles.
 5. The method of claim 1, wherein depositing conductive nanoparticles includes depositing platinum nanoparticles.
 6. The method of claim 1, wherein depositing conductive nanoparticles includes depositing ruthenium nanoparticles.
 7. The method of claim 1, wherein depositing conductive nanoparticles includes depositing cobalt nanoparticles.
 8. The method of claim 1, wherein depositing conductive nanoparticles includes depositing conductive ruthenium oxide nanoparticles.
 9. The method of claim 1, wherein depositing conductive nanoparticles on the dielectric layer by a plasma-assisted deposition process includes depositing conductive nanoparticles on the dielectric layer by plasma-enhanced chemical vapor deposition.
 10. The method of claim 1, wherein depositing conductive nanoparticles on the dielectric layer by a plasma-assisted deposition process includes depositing conductive nanoparticles on the dielectric layer by plasma agglomerated atomic layer deposition.
 11. The method of claim 1, wherein depositing conductive nanoparticles on the dielectric layer by a plasma-assisted deposition process includes depositing conductive nanoparticles on the dielectric layer by physical vapor deposition.
 12. The method of claim 1, wherein depositing conductive nanoparticles on the dielectric layer includes configuring the conductive nanoparticles having a non-planar structure.
 13. The method of claim 12, wherein configuring the conductive nanoparticles having a non-planar structure includes depositing the conductive nanoparticles on a protrusion extending from the dielectric layer.
 14. The method of claim 1, wherein the method includes forming a dielectric layer over the conductive nanoparticles by atomic layer deposition.
 15. The method of claim 1, the method includes forming a dielectric layer over the conductive nanoparticles at a temperature below 600° C.
 16. The method of claim 1, wherein the method includes forming a transistor having the conductive nanoparticles as a gate.
 17. The method of claim 16, wherein forming a transistor having the conductive nanoparticles as a gate a transistor includes forming the conductive nanoparticles as a floating gate.
 18. The method of claim 1, wherein the method includes forming the conductive nanoparticles as a charge storage layer in a memory device.
 19. The method of claim 1, wherein the method includes forming connections to couple the integrated circuit to components of an electronic system.
 20. The method of claim 1, wherein the method includes annealing the conductive nanoparticles to form isolated enlarged islands of agglomerated conductive nanoparticles.
 21. A method of forming an electronic device, the method comprising: forming a dielectric layer in an integrated circuit on a substrate; and depositing conductive nanoparticles on the dielectric layer by atomic layer deposition such that each conductive nanoparticle is isolated from the other conductive nanoparticles, the conductive nanoparticles configured as charge storage elements.
 22. The method of claim 21, wherein depositing conductive nanoparticles by atomic layer deposition includes depositing platinum nanoparticles by atomic layer deposition.
 23. The method of claim 22, wherein the method includes forming a transistor having the platinum nanoparticles as a gate.
 24. The method of claim 23, wherein forming a transistor having the platinum nanoparticles as a gate a transistor includes forming the platinum nanoparticles as a floating gate.
 25. The method of claim 23, wherein the method includes forming the platinum nanoparticles as a charge storage layer in a memory device.
 26. The method of claim 22, wherein the method includes forming connections to couple the integrated circuit to components of an electronic system.
 27. A method of forming an electronic device, the method comprising: forming a dielectric layer in an integrated circuit on a substrate; and depositing platinum nanoparticles on the dielectric layer by a plasma-enhanced chemical vapor deposition process such that each platinum nanoparticle is isolated from the other platinum nanoparticles, the platinum nanoparticles configured as charge storage elements.
 28. The method of claim 27, wherein depositing platinum nanoparticles on the dielectric layer by a plasma-enhanced chemical vapor deposition process includes using (CH₃)₃(CH₃C₅H₄)Pt and O₂ as precursors.
 29. The method of claim 27, wherein depositing platinum nanoparticles on the dielectric layer by a plasma-enhanced chemical vapor deposition process includes using a (CH₃)₃(CH₃C₅H₄)Pt precursor and one or more precursors of N₂O, O₃, or NO.
 30. The method of claim 27, wherein depositing platinum nanoparticles on the dielectric layer by a plasma-enhanced chemical vapor deposition process includes using an argon plasma.
 31. The method of claim 27, wherein depositing platinum nanoparticles includes depositing the platinum nanoparticles having a density of about 100 to 110 nanoparticles per 50 nm×50 nm area.
 32. The method of claim 27, wherein the method includes controlling platinum nanoparticle size by selectively annealing the platinum nanoparticles.
 33. The method of claim 32, wherein selectively annealing the platinum nanoparticles includes annealing the platinum nanoparticles in a N₂O environment at temperatures up to 650° C.
 34. The method of claim 32, wherein selectively annealing the platinum nanoparticles includes annealing the platinum nanoparticles in a NH₃ environment at temperatures up to 850° C.
 35. The method of claim 32, wherein selectively annealing the platinum nanoparticles includes annealing the platinum in an environment and at a temperature to agglomerate platinum nanoparticles to form larger particles with increased spacing between the larger particles.
 36. A method of forming an electronic device, the method comprising: forming a dielectric layer in an integrated circuit on a substrate; and depositing platinum nanoparticles on the dielectric layer by a physical deposition process using a plasma such that each platinum nanoparticle is isolated from the other platinum nanoparticles, the platinum nanoparticles configured as charge storage elements.
 37. The method of claim 36, wherein using a plasma includes using an argon plasma.
 38. The method of claim 36, wherein using a plasma includes applying dosing periods ranging from about one to about two seconds.
 39. The method of claim 36, wherein the method includes controlling platinum nanoparticle size by selectively annealing the platinum nanoparticles.
 40. The method of claim 39, wherein selectively annealing the platinum nanoparticles includes annealing the platinum in an environment and at a temperature to agglomerate platinum nanoparticles to form larger particles with increased spacing between the larger particles.
 41. A method of forming an electronic device, the method comprising: forming a dielectric layer in an integrated circuit on a substrate; and depositing ruthenium nanoparticles on the dielectric layer by a plasma-enhanced chemical vapor deposition process such that each ruthenium nanoparticle is isolated from the other ruthenium nanoparticles, the ruthenium nanoparticles configured as charge storage elements.
 42. The method of claim 41, wherein depositing ruthenium nanoparticles on the dielectric layer by a plasma-enhanced chemical vapor deposition process includes using a (C₆H₈)Ru(CO)₃ precursor.
 43. The method of claim 41, wherein depositing ruthenium nanoparticles on the dielectric layer by a plasma-enhanced chemical vapor deposition process includes using an argon plasma.
 44. The method of claim 41, wherein depositing ruthenium nanoparticles includes depositing the ruthenium nanoparticles having a density of about 100 to 110 nanoparticles per 50 nm×50 nm area.
 45. The method of claim 41, wherein the method includes controlling ruthenium nanoparticle size by selectively annealing the ruthenium nanoparticles.
 46. The method of claim 45, wherein selectively annealing the ruthenium nanoparticles includes annealing the ruthenium in an environment and at a temperature to agglomerate ruthenium nanoparticles to form larger particles with increased spacing between the larger particles.
 47. A method of forming an electronic device, the method comprising: forming a dielectric layer in an integrated circuit on a substrate; and depositing cobalt nanoparticles on the dielectric layer by a plasma agglomerated atomic layer deposition process such that each cobalt nanoparticle is isolated from the other cobalt nanoparticles, the cobalt nanoparticles configured as charge storage elements.
 48. The method of claim 47, wherein depositing cobalt nanoparticles on the dielectric layer by an atomic layer deposition process includes using a C₅H₅CO(CO)₂ precursor and one or more of a NH₃ precursor or a H₂ precursor.
 49. The method of claim 47, wherein depositing cobalt nanoparticles on the dielectric layer by an atomic layer deposition includes using an argon plasma at the completion of a number of ALD cycles.
 50. The method of claim 49, wherein using an argon plasma at the completion of a number of ALD cycles includes using an argon plasma at the completion of ten ALD cycles.
 51. The method of claim 47, wherein depositing cobalt nanoparticles includes depositing the cobalt nanoparticles having a density of about 100 to 110 nanoparticles per 50 nm×50 nm area.
 52. A method of forming a memory, the method comprising: forming an array of memory cells, each memory cell having a charge storage unit structured by: forming a dielectric layer on a substrate; and depositing conductive nanoparticles on the dielectric layer by a plasma-assisted deposition process such that each conductive nanoparticle is isolated from the other conductive nanoparticles, the conductive nanoparticles configured as charge storage elements.
 53. The method of claim 52, wherein depositing conductive nanoparticles includes depositing the conductive nanoparticles such that spacing between the conductive nanoparticles is at about an effective diameter of a conductive nanoparticle.
 54. The method of claim 52, wherein depositing conductive nanoparticles includes depositing metal nanoparticles.
 55. The method of claim 52, wherein depositing conductive nanoparticles includes depositing conductive metal oxide nanoparticles.
 56. The method of claim 52, wherein depositing conductive nanoparticles includes depositing platinum nanoparticles.
 57. The method of claim 52, wherein depositing conductive nanoparticles includes depositing ruthenium nanoparticles.
 58. The method of claim 52, wherein depositing conductive nanoparticles includes depositing cobalt nanoparticles.
 59. The method of claim 52, wherein depositing conductive nanoparticles includes depositing conductive ruthenium oxide nanoparticles.
 60. The method of claim 52, wherein the method includes forming a dielectric layer over the conductive nanoparticles by atomic layer deposition.
 61. The method of claim 52, the method includes forming a dielectric layer over the conductive nanoparticles at a temperature below 600° C.
 62. The method of claim 52, wherein the method includes forming a transistor having the conductive nanoparticles as a floating gate.
 63. A method of forming an electronic system, the method comprising: providing a controller; and coupling an electronic apparatus to the controller, wherein one or both of the controller or the electronic apparatus are formed by a method including: forming a dielectric layer on a substrate; and depositing conductive nanoparticles on the dielectric layer by a plasma-assisted deposition process such that each conductive nanoparticle is isolated from the other conductive nanoparticles, the conductive nanoparticles configured as charge storage elements.
 64. The method of claim 63, wherein depositing conductive nanoparticles includes depositing the conductive nanoparticles such that spacing between the conductive nanoparticles is at about an effective diameter of a conductive nanoparticle.
 65. The method of claim 63, wherein depositing conductive nanoparticles includes depositing metal-nanoparticles.
 66. The method of claim 63, wherein depositing conductive nanoparticles includes depositing conductive metal oxide nanoparticles.
 67. The method of claim 63, wherein depositing conductive nanoparticles includes depositing nanoparticles of a conductive compound.
 68. The method of claim 63, wherein the method includes forming a transistor having the conductive nanoparticles as a floating gate.
 69. An electronic device comprising: a dielectric layer in an integrated circuit; and conductive nanoparticles on the dielectric layer such that each conductive nanoparticle is isolated from the other conductive nanoparticles, the conductive nanoparticles configured as charge storage elements.
 70. The electronic device of claim 69, wherein the conductive nanoparticles are configured in a non-planar arrangement.
 71. The electronic device of claim 69, wherein the conductive nanoparticles include metal nanoparticles.
 72. The electronic device of claim 69, wherein the conductive nanoparticles include conductive metal oxide nanoparticles.
 73. The electronic device of claim 69, wherein the conductive nanoparticles include nanoparticles of a conductive compound.
 74. The electronic device of claim 69, wherein the conductive nanoparticles include platinum nanoparticles.
 75. The electronic device of claim 69, wherein the conductive nanoparticles include ruthenium nanoparticles.
 76. The electronic device of claim 69, wherein the conductive nanoparticles include conductive ruthenium oxide nanoparticles.
 77. The electronic device of claim 69, wherein the conductive nanoparticles include cobalt nanoparticles.
 78. The electronic device of claim 69, wherein the electronic device includes a transistor having the conductive nanoparticles as a gate.
 79. The electronic device of claim 78, wherein the gate is a floating gate.
 80. The electronic device of claim 69, wherein the conductive nanoparticles are configured as a charge storage layer in a memory.
 81. The electronic device of claim 69, wherein the electronic device includes connections to components of an electronic system. 